Fabrikasi Kaca Tellurite Zinc Bismuth Dengan Teknik Melt Quenching


Wahyudi, Wahyudi, Angraeni, Lia



Article Info

Publish Date
02 Jul 2018

Abstract

Penelitian ini betujuan untuk memfabrikasi kaca Tellurite Zinc Bismuth (TZB) denga teknik melt quenching dan mendeskripsikan mengenai kondisi fisika (warna dan transparansi) kaca TZB. Bahan kaca yang digunakan dalam penelitian ini yakni serbuk Tellurite Oxide (TeO2) dengan kemurnian 99,99%, serbuk Zinc Oxide (ZnO) dengan kemurnian 99,9%, dan serbuk Bismut Oxide (Bi2O3) dengan kemurnian 99,9%. Komposisi yang digunakan adalah (80-x)TeO2-20ZnO-xBi2O3 dengan x=8,12,16  (mol%). Tahapan penelitian meliputi penyiapan alat dan bahan, pembuatan sampel dan karakterisasi sampel. Bahan dilebur di dalam furnace CARBOLITETM pada suhu 900oC selama 1 jam kemudian dituang ke dalam mold (cetakan) berukuran (3,5x2,5x0,5) cm yang telah dipanaskan pada suhu 300oC dan didinginkan secara natural cooling. Kaca TZB hasil fabrikasi seperti tampak transparan. Semua sampel kaca yang terbentuk berwarna kuning kehijauan (lime). Perlu dilakukan analisis lebih lanjut berupa UV-VIS untuk menentukan secara pasti pengaruh konsentrasi Bi2O3 sifat optis kaca TZB yang telah difabrikasi.  This research aims to fabricate Tellurite Zinc Bismuth (TZB) glass with melt quenching technique and to describe the physical condition (color and transparency) of TZB glass. The glass materials used in this research are Tellurite Oxide (TeO2) powder with 99.99% purity, 99.9% powder of Zinc Oxide (ZnO), and Bismuth Oxide (Bi2O3) powder with 99.9% purity. The composition used is (80-x) TeO2-20ZnO-xBi2O3 with x = 8.12,16 (mol%). Research stages include preparation of tools and materials, sample preparation and sample characterization. The material is melted in a CARBOLITETM furnace at 900°C for 1 hour then poured into a mold (sized) size (3.5x2.5x0.5) cm which has been heated at a temperature of 300oC and cooled by natural cooling. TZB glass fabrication results as it looks transparent. All glass samples are formed in greenish yellow (lime). Further analysis of UV-VIS is necessary to determine the exact effect of Bi2O3 concentration of the fabricated optical properties of glass TZB.


Copyrights © 2018







Original Source : http://ppjp.unlam.ac.id/journal/index.php/bipf/article/view/4910
Google Scholar : Check in googleschoolar