ANALISIS GMR Ag-Fe PADA PEMBUATAN BAHAN SENSORMEDAN MAGNET DENGAN METODA IMPLANTASI ION

Istiyono, Edi ( Universitas Negeri Yogyakarta )



Article Info

Publish Date
01 Sep 2015

Abstract

The national instrumental industries need support materials that have goodelectrical and magnetic properties. One is for sensor to measure magnetic field,  i. e.: magnetic layer. The experiment is to find  material for  magneticlayer that has high GMR ratio requiredfor sensor. The sample is an Ag-Fe thin film produced by ion implantation: silver implanted with iron ions at various doses from  1.5 x 1017 ions/em to 9.0 x 1017 ions/em and energyfrom 40 ke V to 100 ke V GMR is determined by four-point probe method inmagneticfield  Based on data analysis is conclused that: (1) Increasing of iron ions in Ag-Fe that produced by ion implantation causes decreasing of resistivity. Initially, increasing of annealing temperature causes decreasing of resistivity to minimum point, then the resistivity increases by increasing of annealing temperature; (2) Influence of ions dose, energy and annealing temperature to GMR: (a) Initially, increasing of iron ions increases GMR ratio to the maximum point, then the GMR ratio decreases, (b) Increasing of the ion energy that is used the GMR ratio produced decreases and (c) Increasing of annealing temperature can rise GMR ratio; (3) Ag-Fe for ion. dose of 6. 0 x 1017  ions/em, energy of 100 ke),  and annealing temperatureat 300 C has a minimum resistivity of (16.7 :f: 3) x 10.9 f2m and optimum of GMR ratio  of  6.49%.   Ag-Fe  in  the  condition  is  a good  material fot: magneticfield sensor; and (4) the curves of magnetoresistance are simetry and maximum resistance about magneticfield equal to zero.Keywords: sensor, ion implantation, ion dose, and GMR

Copyrights © 2003