KAJIAN INTERAKSI ION Co2+ DENGANSELULOSA DARI SERBUK GERGAJIKAYU

Mohadi, Risfidian ( Jurusan Kimia FMIPA Universitas Sriwijaya, Kampus Indralaya Km. 32, Ogan Ilir, Sumatera Selatan 30662, Indonesia )
Hidayati, Nurlisa ( Jurusan Kimia FMIPA Universitas Sriwijaya, Kampus Indralaya Km. 32, Ogan Ilir, Sumatera Selatan 30662, Indonesia )
Saputra, Adi ( Jurusan Kimia FMIPA Universitas Sriwijaya, Kampus Indralaya Km. 32, Ogan Ilir, Sumatera Selatan 30662, Indonesia )
Lesbani, Aldes ( Jurusan Kimia FMIPA Universitas Sriwijaya, Kampus Indralaya Km. 32, Ogan Ilir, Sumatera Selatan 30662, Indonesia )



Article Info

Publish Date
14 Nov 2013

Abstract

Telah dilakukan pemisahan selulosa dari serbuk gergaji kayu dengan menggunakan metanol dan HCldengan konsentrasi1%, 3%, 7%, dan 11%(v/v) dalam waktu 3 jam. Selulosa hasil pemisahan dikarakterisasi dengan spektroskopi FT-IR untuk selanjutnya digunakan sebagai adsorben ion logam Co2+ dalam medium air. Proses adsorpsi dipelajari melalui berbagai waktu interaksi, variasi konsentrasi, dan desorpsi terpisah. Spektrum infra merah menunjukan bahwa selulosa hasil pemisahan dari serbuk gergaji kayu dengan konsentrasi asam 5% memiliki kemiripan dengan spektrum inframerah selulosa standar. Konstanta laju adsorpsi ion logam Co2+ pada selulosa hasil pemisahan sebesar2.10-4 denganenergy adsorpsi sebesar 31,54 kJ/molserta pada serbuk gergaji kayu sebesar 4.10-4 dengan energy adsorpsi31,00kJ/mol. Kapasitas adsorpsi ion logam Co2+pada selulosa hasil pemisahan sebesar 0,55 x10-4 mol/g dan 0,09 x10-4mol/g untuk serbuk gergaji kayu. Desorpsi terpisah ion logam Co2+ menggunakan H2O, Na-EDTA, Amonium asetat, dan HCl menunjukan interaksi yang kuat ion logam Co2+ pada selulosa dan serbuk kayu. Separation of cellulosefrom wood sawdust using methanol and hydrocloric acid in acid concentrations of 1%, 3%, 7%, dan 11%(v/v) for 3 hours has been carried out. The cellulose was characterized using FT-IR spectroscopy and used as adsorbent for Co2+ metal ion in aqueous medium. Adsorption process was studied by varying the interaction time, concentration of solution, and desorption. The FT-IR spectrum of cellulose obtained from wood using 5% HCl has similarity withFT-IR spectrum of the standardcellulose. The adsorption rate constant and adsorption energy ofCo2+on cellulose obtained from wood sawdustare 2.10-4 and31,54 kJ/mol respectively,meanwhile those values are4.10-4  and 31.00 kJ/mol respectively on raw wood sawdust.The adsorption capacity  of cellulose andof wood sawdust are 0,55 x10-4 mol/g and 0,09 x10-4mol/g, respectively.The separated desorption of Co2+ metal ion using H2O, Na-EDTA, Amonium acetic, and HCl showedthat Co2+wasstrongly bound to cellulose and wood sawdust.

Copyrights © 2013






Journal Info

Abbrev

cakra

Publisher

Subject

Chemical Engineering, Chemistry & Bioengineering Chemistry Electrical & Electronics Engineering

Description

Jurnal ini merupakan jurnal elektronik di bidang kimia terapan yang dikelola oleh Magister Kimia Terapan, Program Pascasarjana, Universitas Udayana, Bali. Jurnal ini memuat artikel-artikel penelitian yang berhubungan dengan Kimia Terapan yang meliputi Kimia Analitik, Kimia Polimer, Biokimia, Kimia ...