KARAKTERISTIK NANOPARTIKEL ZnO: STUDI EFEK PELARUT PADA PROSES HIDROTHERMAL Saragi, Togar; PURBA, YONATAN R; D U, SATRIA AUFFA; OKTAVIANI, MARIA; SUSILAWATI, TUTI; RISDIANA, RISDIANA; BAHTIAR, AYI
Jurnal Material dan Energi Indonesia Vol 6, No 01 (2016): Jurnal Material dan Energi Indonesia
Publisher : Jurnal Material dan Energi Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (356.403 KB)

Abstract

Telah berhasil disintesis nanopartikel ZnO (ZnO-NP) pada pelarut yang berbeda dengan metode hidrotermal. Bahan dasar yang digunakan adalah zinc acetate dihydrate (Zn(CH3COO)2.2H2O, Merck, 99 %), sodium hydroxide (NaOH, Merck), dengan pelarut 2-propanol (Sigma Aldrich, 99%) dan ethanol. Karakterisasi optik, morfologi dan struktur kristal nanopartikel ZnO masing-masing dilakukan melalui pengukuran UV-Vis, TEM dan XRD. Dari hasil pengukuran UV-Vis diperoleh bahwa band gap ZnO-NP pada pelarut 2-propanol memiliki energi band gap yang lebih besar dibandingkan dengan sampel pada pelarut ethanol. Dari hasil pengukuran TEM diperoleh bahwa morfologi nanopartikel ZnO pada pelarut 2-propanol memiliki bentuk nano-rod (20 nm ´ 9 nm), sedangkan nanopartikel ZnO pada pelarut etanol lebih cenderung oval (26 nm ´ 15 nm). Karakteristik kristal nanopartikel ZnO pada kedua pelarut memiliki memiliki struktur kristal hexagonal wurtzite.
KARAKTERISRIK KRISTAL DAN OPTIK NANOPARTIKEL ZINC OXIDE: KAJIAN EFEK MOLARITAS DALAM PROSES HIDROTHERMAL Saragi, Togar; Purba, Yonatan R; Auffa, Satria; Oktaviani, Maria; Simanjuntak, Edward; Susilawati, Tuti; Syakir, Norman; Kartawidjaja, Mariah; Risdiana, Risdiana; Bahtiar, Ayi
Spektra: Jurnal Fisika dan Aplikasinya Vol 1 No 2 (2016): SPEKTRA: Jurnal Fisika dan Aplikasinya, Volume 1 Nomor 2, Desember 2016
Publisher : Program Studi Fisika Universitas Negeri Jakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.21009/SPEKTRA.012.07

Abstract

Abstrak Sintesis nanopartikel Zinc Oxide (ZnO) dengan metode hidrothermal sangat dipengaruhi oleh beberapa parameter, salah satu diantaranya adalah perbandingan prekursor dan katalis dalam pelarut. Dalam penelitian ini telah berhasil disintesis nanopartikel zinc oxide dengan metode hidrothermal. Prekursor yang digunakan adalah zinc acetat dan katalis NaOH dalam pelarut ethanol. Perbandingan molaritas prekursor dan katalis adalah 0,008:0,5 dan 0,3:0,9. Karakteristik optik, morfologi dan struktur kristal nanopartikel ZnO masing-masing dilakukan dengan pengukuran UV-Vis, TEM dan XRD. Nanopartikel yang dihasilkan memiliki memiliki struktur kristal hexagonal wurtzite. Nanopartikel zinc oxide dengan perbandingan 0,3:0,9 memiliki karakteristik yang paling baik dibandingkan dengan nanopartikel dengan perbandingan 0,008:0,5. Reaksi dalam hidrothermal kaitannya dengan perubahan tekanan akibat peningkatan volume akan dikaji lebih jauh. Kata-kata kunci: oksidasi zinc, nanopartikel, hidrotermal, molaritas Abstract Synthesis of Zinc Oxide (ZnO) nanoparticles by hydrothermal method is influenced by several parameters one of them is the ratio of the precursor and catalyst in a solvent. In this study, we have successfully synthesized of zinc oxide nanoparticles by hydrothermal method. The raw material of precursor is zinc acetate, NaOH as catalyst and ethanol as a solvent. The molarity ratio of precursor and catalyst are 0.008: 0.5 and 0.3: 0.9. The optical characteristics, morphology and crystal structure of ZnO nanoparticles were characterised by the UV-Vis, TEM and XRD, respectively. From XRD measurement, it was observed that samples have hexagonal wurtzite structure and all peaks are well fitted with JCPDS:36-1451 data. The growth condition in the ratio of 0.3: 0.9 showed the best sample with high quality crystal structure and rod form. The effect of molar ratio to the characteristics of nanoparticle will be studied further in relation with the change of volume, and pressure inside of the reactor. Keywords: zinc oxide, nanoparticle, hidrotermal, molaritas
KARAKTERISTIK NANOPARTIKEL ZnO: STUDI EFEK PELARUT PADA PROSES HIDROTHERMAL SARAGI, TOGAR; PURBA, YONATAN R; D U, SATRIA AUFFA; OKTAVIANI, MARIA; SUSILAWATI, TUTI; RISDIANA, RISDIANA; BAHTIAR, AYI
Jurnal Material dan Energi Indonesia Vol 6, No 01 (2016)
Publisher : Fakultas Matematika dan Ilmu Pengetahuan Alam

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (356.403 KB) | DOI: 10.24198/jmei.v6i01.9366

Abstract

Telah berhasil disintesis nanopartikel ZnO (ZnO-NP) pada pelarut yang berbeda dengan metode hidrotermal. Bahan dasar yang digunakan adalah zinc acetate dihydrate (Zn(CH3COO)2.2H2O, Merck, 99 %), sodium hydroxide (NaOH, Merck), dengan pelarut 2-propanol (Sigma Aldrich, 99%) dan ethanol. Karakterisasi optik, morfologi dan struktur kristal nanopartikel ZnO masing-masing dilakukan melalui pengukuran UV-Vis, TEM dan XRD. Dari hasil pengukuran UV-Vis diperoleh bahwa band gap ZnO-NP pada pelarut 2-propanol memiliki energi band gap yang lebih besar dibandingkan dengan sampel pada pelarut ethanol. Dari hasil pengukuran TEM diperoleh bahwa morfologi nanopartikel ZnO pada pelarut 2-propanol memiliki bentuk nano-rod (20 nm ´ 9 nm), sedangkan nanopartikel ZnO pada pelarut etanol lebih cenderung oval (26 nm ´ 15 nm). Karakteristik kristal nanopartikel ZnO pada kedua pelarut memiliki memiliki struktur kristal hexagonal wurtzite.