PHASE ANALYSIS AND MAGNETIC PROPERTIES OF BaFe12O19/Nd2Fe14B COMPOSITE BY MECHANICAL MILLING PRODUCT Sardjono, Prijo; Adi, Wisnu Ari; Sebayang, Perdamaian; ., Muljadi
Jurnal Sains Materi Indonesia Vol 13, No 2 (2012): Februari 2012
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (41.834 KB)

Abstract

The synthesis and characterization of BaFe12O19/Nd2Fe14B composite by use mechanical milling has been performed. The result of refinement of X-ray diffractions showed that the sample consist of two phases namely BaFe12O19 and Nd2Fe14B phase with fraction mass were 79.89 and 20.11 wt%, respectively. The BaFe12O19 system magnetic materials have been formed with the crystal structure of hexagonal (space group P 63/m m c), lattice parameter are a = 5.9033(5) Å, b = 5. 9033(5) Å and c = 23.239(2) Å, α = β = 90o and γ = 120o, V = 701.3(1) Å3 and ρ = 5.7172 g.cm-3. The Nd2Fe14B system magnetic materials have been formed with the crystal structure of tetragonal (space group P 42/m n m), lattice parameter are a = 8.865(8) Å, b = 8.865(8) Å and c = 12.269(1) Å, α = β = γ = 90o, V = 964.3(1) Å3 and ρ = 7.7508 g.cm-3. The magnetic properties result of Nd2Fe14B shown that the sample has the coercive field and remanence magnetization are 7984 Oe and 5250 Gauss, respectively. The BaFe12O19 are 1625 Oe and 1190 Gauss, respectively. And the BaFe12O19- Nd2Fe14B composite increase to become 2650 Oe and 1580 Gauss, respectively. We conclude that the process of mixing between BaFe12O19 and Nd2Fe14B is not affect the change of each phase. The BaFe12O19 particle can be use as the shielding of the Nd2Fe14B particle from it’s the corrosion properties. The BaFe12O19 magnetic material has a stable structure at room temperature, so that this structure was not easy of change after mix with the Nd2Fe14B particles.Keywords: BaFe12O19/Nd2Fe14B, Mechanical milling, Crystal structure, Magnetic properties.
ANALISIS FASA DAN SIFAT MAGNETIK PADA KOMPOSIT BaFe12O19/NdFe14B HASIL MECHANICAL MILLING Sardjono, Prijo; Adi, Wisnu Ari; Sebayang, Perdamaian; Muljadi, Muljadi
Jurnal Sains Materi Indonesia Vol 13, No 2: FEBRUARI 2012
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (575.101 KB)

Abstract

ANALISIS FASA DAN SIFAT MAGNETIK PADA KOMPOSIT BaFe12O19/NdFe14B HASIL MECHANICAL MILLING. Telah dilakukan analisis fasa dan uji sifat magnetik pada bahan komposit magnet BaFe12O19/NdFe14B hasil mechanical milling menggunakan difraksi sinar-X dan GmbH Permagraph. Hasil refinement dari pola difraksi sinar-X menunjukkan bahwa sampel terdiri dari 2 fasa, yaitu fasa BaFe12O19 dan fasa NdFe14B. Sedangkan fraksi massa dari fasa BaFe12O19 dan fasa NdFe14B berturut-turut sebesar 79,89 % dan 20,11 %. Sampel bahan magnet BaFe12O19 dengan struktur kristal heksagonal (space group P 63/m m c), parameter kisi α = 5,9033(5) Å, b = 5,9033(5) Å dan c = 23,239(2) Å, α = β = 90o dan  = 120o, V = 701,3(1) Å3 dan  = 5.7172 g.cm-3. NdFe14B dengan struktur kristal simetri tetragonal (space group P 42/m n m (No. 136)) dengan parameter kisi sebesar a = 8,865(8) Å, b = 8,865(8) Å dan c = 12,269(1) Å, α = β = γ = 90o, V = 964,3(1) Å3 dan ρ = 7,7508 g.cm-3. Hasil pengukuran sifat magnetik menunjukkan bahwa bahan magnet NdFe14B sebelum dimilling memiliki medan koersivitas dan medan magnet rimanen berturut turut adalah 7984 Oe dan 5250 Gauss. Sedangkan untuk bahan magnet BaFe12O19 berturut-turut adalah 1625 Oe dan 1190 Gauss. Setelah dimilling selama 30 jam, medan koersivitas dan medan magnet rimanen meningkat di atas bahan magnet BaFe12O19 berturut-turut adalah 2650 Oe dan 1580 Gauss. Disimpulkan bahwa proses pencampuran ini tidak memberikan dampak rusaknya struktur fasa masing-masing. Partikel-partikel BaFe12O19 dapat dijadikan sebagai pelindung dari partikel-partikel NdFe14B yang memiliki sifat yang sangat korosif pada suhu kamar. Fasa BaFe12O19 ini relatif stabil pada suhu kamar sehingga partikel-partikel BaFe12O19 tidak mudah berubah setelah bercampur dengan partikel-partikel NdFe14B.