PREPARASI MAGNET SINTER Pr-Fe-B DENGAN MENGGUNAKAN SPARK PLASMA SINTERING Sudiro, Toto; Sardjono, Priyo; Thosin, Kemas Ahmad Zaini; Muljadi, Muljadi
Telaah Vol 32, No 1 (2014)
Publisher : Research Center for Physics

Show Abstract | Original Source | Check in Google Scholar

Abstract

Penelitian ini bertujuan untuk mempreparasi sinter Pr-Fe-B dengan teknik spark plasma sintering (SPS). Proses fabrikasi dilakukan di dalam ruang vakum bertekanan kurang dari 60 Pa di mana powder dikompaksi padatekanan 40 MPa pada temperatur yang berbeda: 800 oC, 900 oC, dan 1050 oC. Komposisi fase dari kompak material tersebut dianalisis dengan X-ray diffractometer (XRD Shimadzu-7000TM;). Sampel kemudian dimagnetisasi dengan impulse magnetizer K-series, Magnet-Physik Dr. Steingroever GmbHTM. Hasil penelitian menunjukkan bahwa dengan meningkatnya temperatur SPS, kuat medan magnet permukaannya menurun. Hal ini diduga disebabkan oleh pembentukan Fe phase yang memiliki sifat buruk terhadap properti magnet Pr-Fe-B.
PEMBUATAN MAGNET PERMANEN BONDED Nd2Fe14B DENGAN PEREKAT SILICON RUBBER DAN KARAKTERISASINYA Muljadi, Muljadi; Sardjono, Priyo
Telaah Vol 32, No 1 (2014)
Publisher : Research Center for Physics

Show Abstract | Original Source | Check in Google Scholar

Abstract

Telah dibuat magnet permanen Nd2Fe14B yang dibuat dari pencampuran serbuk NdFeB dengan perekat pasta silicon rubber (SR). Persentase berat SR divariasikan sebesar 5, 10, 15, dan 20%. Karakterisasi yang dilakukan meliputi pengukuran bulk density, analisis mikrostruktur dengan SEM, dan pengukuran sifat magnetik dengan menggunakan gaussmeter dan B-H curve permagraph. Hasil XRD serbuk Nd2Fe14B yang digunakan sebagai bahan baku menunjukkan bahwa terdapat dua fase yaitu fasa Nd2Fe14B dan fase Fe sebagai fase minor. Komposisi SR juga memberikan pengaruh yang signifikan terhadap bulk density, mikrostruktur, dan sifat magnetiknya. Sampel dengan 5% berat SR memiliki bulk density terbesar, yaitu 4.67 g/cm3. Sebaliknya, sampel dengan 20% berat SR memiliki nilai bulk density terendah, yaitu 3.12 g/cm3 . Hasil pengukuran sifat magnetik menunjukkan bahwa semakin banyak persentase SR, maka sifat magnetiknya cenderung menurun.  Nilai tertinggi flux density sekitar 1070 G dan nilai remanensi Br adalah 4.85 kG pada sampel dengan 5% berat SR. Di sisi lain, sampel dengan 20% berat SR memiliki nilai flux density dan remanensi terendah, yaitu masing-masing sebesar 450 G dan 2.47 kG.
MECHANICAL AND MAGNETIC PROPERTIES OF BONDED MAGNET Nd2Fe14B PRODUCED USING BINDER BAKELITE Muljadi, -; Sardjono, Priyo; Sebayang, Perdamean
Teknologi Indonesia Vol 37, No 3 (2014)
Publisher : LIPI Press

Show Abstract | Original Source | Check in Google Scholar | Full PDF (16.051 KB)

Abstract

Bonded magnet Nd2Fe14B was made with mixing Nd2Fe14B powder and polymer bakelite using compressing method. The bakelite concentration was varied of 5 wt%, 10 wt%, 15 wt%, and 20 wt%. Both Nd2Fe14B and bakelite powders were mixed and milled for 24 hours using a ball mill. The powder was formed by dry pressing and subsequently dried in a drying cabinet at a temperature of 180oC for 4 hours. Then, magnetization process was done using impulse magnetizer, and performed measurements of the magnetic properties such as flux density, remanenceBr, coercivity Hic and energy density (BH)max using Gaussmeter and hysteresis permeagraph. Characterization of mechanical properties such as bending strength (BS) and vickers hardness (Hv) was determined before magnetization. Bakelite concentration had a significant influence on both magnetic and mechanical properties. From the characterization results, the optimum concentration of bakelite was 10% and 15% wt. Bonded Nd2Fe14B magnet obtained had the following properties: BS value of 27.7433.42 MPa, Hv value of 292.65314.33 MPa, the value of the magnetic flux density from 1360 to 1400 Gauss, remanence Br = 4.995:02 kG, coercivity Hic = 7.8 kOe, and energy density (BH)max about 5.13 to 5.24 MGOe at the optimum concentration.
THE EFFECT OF LI2O ONCOMPOSITE LTAP AND WINDOWS GLASSES Prihandoko, Bambang; Sardjono, Priyo; Zulfia, Anne; Siradj, Eddy
Jurnal Sains Materi Indonesia Vol 9, No 1: OKTOBER 2007
Publisher : Center for Science & Technology of Advanced Materials - National Nuclear Energy Agency

Show Abstract | Original Source | Check in Google Scholar | Full PDF (454.844 KB)

Abstract

THE EFFECT OF LI2O ONCOMPOSITE LTAP AND WINDOWS GLASSES. Research on The Effect of Li2O on Composite LTAP and Windows Glasses have been done. Windows glasses contain of SodiumLime Silica Glasses and Na2O 11,6%, CaO 8,1%and SiO2 58,7%. LTAP ( Lithium Titanium Alumunium Phosphate ) material mixed in the slurry of powder windows glasses with composition of weight procentage 75%. The temperatures process for sintering of samples is above of glass transition at 600 oC. Then samples quenched with liquid nitrogen. The variation of Li2O addition on samples are 0, 2,5, 5 and 7,5% weight. XRD pattern of all samples has a same phenomenon of crystallization phases, i.e. LTAP with lithium silica from Li5Si2O7, Li2SiO3, Li4SiO4 and Li2Si2O5. Optimum addition oh Li2O is 7,5% weight Li2O that gift a conductivity of 1,479 x 10-7 S/cm and high value on density and smallest porosity
Pembuatan dan Pengujian Bulk Density, Fluks Magnetik, dan Mikrostruktur pada Hybrid Magnet Berbasis NdFeB / BaFe12O19 Djuhana, Djuhana; Muljadi, Muljadi; Sunardi, Sunardi; Sardjono, Priyo
PISTON: Journal of Technical Engineering Vol 1, No 2 (2018): PISTON: JOURNAL OF TECHNICAL ENGINEERING
Publisher : Prodi Teknik Mesin

Show Abstract | Original Source | Check in Google Scholar | Full PDF (747.059 KB)

Abstract

Telah dilakukan pembuatan hybrid magnet permanen berbasis NdFeB dengan penambahan BaFe12O19 ( 5, 10, 15, dan 20 % wt). Aplikasi hybrid magnet permanen NdFeB untuk komponen motor dan generator listrik skala kecil. Tujuan penelitian ini adalah untuk mengetahui pengaruhnya penambahan BaFe12O19 terhadap densitas, fluks magnetik dan mikrostruktur dari hybrid magnet NdFeB. Proses preparasi bahan baku mulai dari pencampuran serbuk NdFeB tipe MQP-B+ dengan BaFe12O19, digerus dan dicampur bahan perekat Epoxy Resin sebanyak 6 %wt dan dicetak dengan gaya 8 tonf sehingga membentuk pellet dengan diameter 18,5 dan tebal 4,3 mm. Sampel yang telah dicetak kemudian dikeringkan pada kondisi vacuum (±15 mbar) dengan temperatur 80°C ditahan selama 1 jam. Karakterisasi yang dilakukan meliputi pengukuran bulk density, microstructurer menggunakan Optical Microscope dan sifat magnet dengan menggunakan Gaussmeter. Dari hasil karakterisasi secara keseluruhan diperoleh kondisi optimum pada komposisi hybrid magnet NdFeB adalah 95% NdFeB, 5 %wt BaFe12O19 . Sifat-sifat hybrid magnet NdFeB tersebut adalah bulk density = 4,469  g/cm3, Fluks magnetik = 1029,85 Gauss, ukuran bulir (grain size) sekitar 4,1 – 5,2 µm.