SYNTHESIS OF FERRITE NANOPARTICLE BY MILLING PROCESS FOR PREPARATION OF SINGLE DOMAIN MAGNET

Jurnal Sains Materi Indonesia Vol 11, No 1 (2009): Oktober 2009
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar

Abstract

Study of ferrite nanoparticle synthesis for preparation of single domain magnet by milling of scrap magnet material have been done. Sample preparation were done using disk mill continued with high energy milling (HEM). Some powder were taken after 5, 10 dan 20 hours milling using HEM-E3D. The powder were then characterized using X-Ray Fluorescence (XRF), X-Ray Diffractometer (XRD) and Scanning Electron Microscope (SEM). XRF characterization result, confirmed by XRD analysis result, showed that the sample are of Strontium ferrite phase. Microstructure analysis result showed the occurence of grain refining process of ferrite particle with increasing of milling time. Particle having size of nanometers successfully obtained, although in unhomogeneous distribution. Magnetic properties characterization result showed the increasing of hysteresis curve area of sample for longer milling time and sintering process. Keywords: Strontium Ferrite, Nanoparticle, Milling, Single domain magnet.

PENGARUH DOPING NI TERHADAP RESISTIVITAS SENYAWA LA0.67SR0.33MN1-XNIXO3

Spektra: Jurnal Fisika dan Aplikasinya Vol 1 No 2 (2016): SPEKTRA: Jurnal Fisika dan Aplikasinya, Volume 1 Nomor 2, Desember 2016
Publisher : Program Studi Fisika Universitas Negeri Jakarta

Show Abstract | Original Source | Check in Google Scholar | Full PDF (401.581 KB)

Abstract

Abstrak Penelitian terhdap sifat listrik material  lanthanum manganat telah dilakukan. Perubahan sifat listrik senyawa mixed valence manganites dipengaruhi oleh pemberian doping pada site La dan Mn. Dalam penelitian kali ini, senyawa La0,67Sr0,33Mn1-xNixO3 dibuat dengan metode sintesa sol gel. Senyawa yang dibuat kemudian dikarakterisasi dengan menggunakan X-Ray Diffractometer (XRD) untuk mengetahui struktur sampel, selanjutnya diuji dengan menggunakan cryogenic magnetometer untuk mengukur resistivitas sampel sebagai fungsi temperatur. Hasil karakterisasi XRD menunjukkan bahwa senyawa yang dibentuk memiliki struktur Rhombohedral dengan space group R-3c dan ukuran kristalit kurang dari 100 nm. Pemberian doping Ni tidak merubah struktur kristal namun berpengaruh terhadap penurunan parameter kisi kristal dan ukuran kristalit. Hasil pengukuran resistivitas menunjukkan bahwa senyawa yang diuji berperilaku sebagai isolator dan doping Ni meningkatkan resistivitas sampel. Kata-kata kunci: Resistivitas, mixed valence manganites, doping Ni, metode sol gel. Abstract Transport properties of lanthanum manganites have been studied. Mixed valence manganites material transport properties changed with doping at La and Mn site. In this study, La0,67Sr0,33Mn1-xNixO3 material was synthesized using sol gel method. These samples were characterized using X-Ray Diffractometer (XRD) to investigate the structure of samples. While the resistivity of samples as a function of temperature was measured using cryogenic magnetometer. XRD result showed that samples were having Rhombohedral structure with R-3c space group and crystallite size smaller than 100 nm. Ni doping have not changed crystal structure but decreased lattice parameter and size of the crystal. Resistivity measurement result showed insulator behavior of the samples and Ni doping enhanced the resistivity of samples. Keywords: Resistivity, mixed valence manganites, Ni doped, sol gel method.

Microwave Absorber Properties \ce {La_{0.67}Sr_{0.33}Mn_{0.8}Ni_{0.2}O3} Using Sol Gel Synthesis Methods

Omega: Jurnal Fisika dan Pendidikan Fisika Vol 3 No 2 (2017)
Publisher : Program Studi Pendidikan Fisika UHAMKA

Show Abstract | Original Source | Check in Google Scholar | Full PDF (317.449 KB)

Abstract

This paper reports the process and the results are supplemented by material microwave absorber characterisation \ce {La_{0.67}Sr_{0.33}Mn_{0.8}Ni_{0.2}O3} which has been synthesised by sol gel method. Results refinement of the XRD data showed that the material \ce {La_{0.67}Sr_{0.33}Mn_{0.8}Ni_{0.2}O3} have formed a single phase. From the results of using the software refinement High Score obtained crystal size on sample of 21.18 nm. Number of spin concentration in the sample at ESR test results showed a decrease when doping Ni increased, the area under the curve of absorption decreases as 388.718. This is due to the substitution of \ce {Ni^{2+}} ions \ce {Mn^{3+}} ions thus inhibiting electron hopping of electrons $\mathrm{e_g}$ (\ce {Mn^{3+}} ion) to $\mathrm{t_{2g}}$ (\ce {Mn^{4+}} ion) in the mechanism of double exchange so that the spin of the electrons will $\mathrm{t_{2g}}$ antiparallel. Competition between ferromagnetic properties with antiferromagnetic spin make will change the direction so that the sample magnetisation will decrease and the magnetic moments become random. ESR results are used to confirm the results of the VNA. Microwave absorption ability is indicated by the value of reflection loss on the sample is $-66.67$ dB.

SINTESIS NANOPARTIKEL FERIT UNTUK BAHAN PEMBUATAN MAGNET DOMAIN TUNGGAL DENGAN MECHANICAL ALLOYING

Jurnal Sains Materi Indonesia Vol 11, No 1: OKTOBER 2009
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (891.14 KB)

Abstract

SINTESIS NANOPARTIKEL FERIT DENGAN PROSES MILLING UNTUK BAHANPEMBUATAN MAGNET DOMAIN TUNGGAL. Studi sintesis nanopartikel ferit untuk bahan pembuatan magnet domain tunggal dengan menggunakan metode milling dari bahan scrap magnet telah dilakukan. Preparasi sampel dilakukan menggunakan disk mill yang dilanjutkan dengan menggunakan High Energy Ball mill (HEM-E3D) dengan waktu milling 5 jam, 10 jam dan 20 jam. Sampel tersebut selanjutnya dikarakterisasi menggunakan X-Ray Fluorescence (XRF), X-Ray Diffractometer (XRD) dan Scanning Electron Microscope (SEM). Hasil karakterisasi XRF yang dikonfirmasi dengan hasil analisis XRD menunjukkan bahwa sampel magnet adalah stronsium ferit. Hasil analisis struktur mikro memperlihatkan terjadinya proses penghalusan ukuran partikel ferit dengan bertambahnya waktu milling. Partikel berukuran nanometer berhasil diperoleh,meskipun distribusinya tidak homogen. Hasil karakterisasi sifat magnetik dari sampel hasil milling yang kemudian disintering menunjukkan peningkatan daerah kurva histeresis pada sampel dengan waktu milling yang lebih lama

MICROWAVE ABSORBING PROPERTIES OF LaMn1-x NixO3.

Jurnal Sains Materi Indonesia Vol 15, No 4: JULI 2014
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (230.577 KB)

Abstract

MICROWAVE ABSORBING PROPERTIES OF LaMn1-x NixO3. The doped lanthanum manganites have unusual magnetic and transport properties, which makes it possible for this material to be used for microwave absorbing. In this study, LaMn1-xNixO3 (x = 0, 0.02, 0.04, and 0.06) were prepared by solid state reaction method as microwave absorption material. The crystal structure and magnetic properties were characterized byX-Ray Diffractometer (XRD) and Vibrating SampleMagnetometer (VSM), respectively. Refinement results of X-Ray diffraction pattern using High Score Plus Software showed that the samples with various x = 0 to x = 0.04 had a single phase with monoclinic crystal structure, while the sample with x = 0.06 had two phases with monoclinic and hexagonal structures. Hysteresis loops showed that the LaMn1-xNixO3 (x = 0, 0.02, 0.04, and 0.06) samples are soft magnetic materials. Microwave absorption properties were investigated in the frequency range of 8-12 GHz using Vector Network Analyzer (VNA). An optimal reflection loss of -8.85 dB is reached at 11.58 GHz for x = 0.04 with sampel thickness of 2 mm.

PREDIKSI KUALITATIFMATURITAS MATERIALORGANIK DI DALAM SEDIMEN SUMUR MINYAK BUMI DENGAN RESONANSI SPIN ELEKTRON.

Jurnal Sains Materi Indonesia Vol 6, No 2: FEBRUARI 2005
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (238.342 KB)

Abstract

PREDIKSI KUALITATIFMATURITAS MATERIALORGANIK DI DALAM SEDIMEN SUMUR MINYAK BUMI DENGAN RESONANSI SPIN ELEKTRON. Dengan metode Resonansi Spin Elektron (RSE) dapat dideteksi adanya kandungan bahan paramagnetik dan radikal bebas di dalam sedimen sumur minyak bumi. Pengukuran konsentrasi radikal bebas sebagai fungsi kedalaman sumur atau suhu dapat memberikan informasi tentang maturitas material organik di dalam sedimen. Hasil pengamatan RSE menunjukkan bahwa sedimen dari Tuban (kedalaman 1450 m) mengandung ion Mn+2, sedangkan sedimen dari Kalimantan Timur (1310 m) tidak mengandung ion paramagnet. Sampel memberikan signal radikal bebas kerogen dengan faktor Lande g = 2,002. Diprediksi bahwa sedimen dari Kalimantan Timur berasal dari kedalaman sumur yang belum mencapai kondisi maturitas maksimal.

MAGNETIC PROPERTIES OF THE TWO-LEG ZIG-ZAG LADDER IN QUANTUM SPIN SYSTEM NH4CuCl3

Jurnal Sains Materi Indonesia VOL 3, NO 2: FEBRUARI 2002
Publisher : Center for Science & Technology of Advanced Material - National Nuclear Energy Agency of

Show Abstract | Original Source | Check in Google Scholar

Abstract

MAGNETIC PROPERTIES OF THE TWO-LEG ZIG-ZAG LADDER IN QUANTUM SPIN SYSTEM NH4CuCl3. Numerical analysis of the two-leg zig-zag ladder as a single chain with next-nearest neighbour interactions has been formulated by Cabra (1999) with the following Hamiltonian: Other formulation for two leg zig-zag ladder with dimmerized chains and coupling between the chains is as follow : From these formulations, we study the closing of the gap at zero magnetization by means of the fine—tuning mechanism and disappreance of the 1/2 plateau (gap) at finite by alternating dimerization of the chains along the rungs. We also described NH4CuCl3 under high magnetic fields in a two-leg system.

GIANT MAGNETORESISTANCE PADA PADUAN CaMnO3

Jurnal Sains Materi Indonesia Edisi Khusus Oktober 2007
Publisher : Center for Science & Technology of Advanced Material - National Nuclear Energy Agency of

Show Abstract | Original Source | Check in Google Scholar

Abstract

GIANT MAGNETORESISTANCE PADA PADUAN CaMnO3. Telah dilakukan sintesis dan karakterisasi GiantMagnetoresistance (GMR) paduan CaMnO3. Sintesis bahan CaMnO3 menggunakan metode Mechanical Alloying. Bahan ini dimilling selama 12 jam dan dilakukan proses pemanasan pada suhu 1000 oC selama 9 jam. Hasil pengukuran dengan difraksi sinar-x (XRD) menunjukkan bahwa paduan CaMnO3 memiliki kualitas yang cukup baik. Hasil foto dengan Scanning Eectron Microscope (SEM) menunjukkan bahwa butir-butir kristal berbentuk bulat-bulat hampir homogen di seluruh permukaan paduan dengan ukuran butiran sekitar 200 nm hingga 300 nm walaupun masih tampak adanya porositas. Paduan CaMnO3 ini memiliki rasio magnetoresistance Δρ/ρ cukup besar sebesar 28%. Disimpulkan bahwa telah diperoleh paduan giant magnetoresistance CaMnO3 yang memiliki sifat magnetoresistance sangat baik. Rasio GMR pada penelitian ini 2 kali hingga 10 kali lebih besar dibandingkan dengan penelitian sebelumnya.

PENGARUH UKURAN BUTIR TERHADAP RASIO MAGNETORESISTANCE PADA PADUAN La0,67Ca0,33Mn0,93Ti0,07O3

Jurnal Sains Materi Indonesia Edisi Khusus Oktober 2007
Publisher : Center for Science & Technology of Advanced Material - National Nuclear Energy Agency of

Show Abstract | Original Source | Check in Google Scholar

Abstract

PENGARUH UKURAN BUTIR TERHADAP RASIO MAGNETORESISTANCE PADA PADUAN La0,67Ca0,33Mn0,93Ti0,07O3. Telah dilakukan sintesis dan karakterisasi Giant Magnetoresistance pada paduan La0,67Ca0,33Mn0,93Ti0,07O3. Sintesis bahan La0,67Ca0,33Mn0,93Ti0,07O3 menggunakan metode reaksi padatan (solid state method) dari oksida-oksida penyusun La2O3, CaCO3, MnO2, dan TiO2 dengan perbandingan stokiometri unsur La : Ca : Mn : Ti = 0,67 : 0,33 : 0,97 : 0,07. Campuran ini dimilling selama 12 jam dan dilakukan proses pemanasan pada suhu 1350 oC selama 6 jam. Bahan ini kemudian dimilling kembali dengan variasi milling 5 jam, 10 jam, 15 jam, 20 jam dan 25 jam dan dilakukan proses pemanasan ulang pada suhu 1100 oC selama 24 jam. Hasil pengukuran dengan difraksi sinar-X (XRD) menunjukkan bahwa sintesis bahan La0,67Ca0,33Mn0,93Ti0,07O3 memiliki fasa tunggal (single phase) dengan struktur kristal ortorombik, space group Pnma (I-62) dan parameter kisi a = 5,474(2) b = 7,727(3) dan c = 5,477(2). Hasil pengukuran menggunakan EDAX menunjukkan bahwa bahan inimemiliki kualitas yang cukup baik dengan komposisi unsur La : Ca : Mn : Ti : O = 15,13 % : 8,28 % : 18,18 % : 1,58 % : 56,33 %. Hasil foto dengan Scanning Electron Microscope (SEM) menunjukkan bahwa butir-butir kristal berbentuk bulat-bulat hampir homogen di seluruh permukaan sampel dengan ukuran butiran sekitar 1000 nm hingga 4000 nm, 250 nm hingga 2000 nm, 250 nm hingga 1000 nm, 250 nm hingga 500 nm, 100 nm hingga 250 nm berturut-turut untuk milling 5 jam, 10 jam, 15 jam, 20 jam, 25 jam. Pada sampel La0,67Ca0,33Mn0,93Ti0,07O3 ini memiliki rasio magnetoresistance cukup besar dengan rasio dρ/ρ sebesar 14,7 %, 18,0 %,24,5 %, 30,8 % 35,2 % dan 44,6%. Telah diperoleh paduan giant magnetoresistance La0,67Ca0,33Mn0,93Ti0,07O3 dengan kualitas yang cukup baik dan ukuran butir sangat mempengaruhi besarnya rasio magnetoresistance hingga 3 kali lipat dari sebelumnya. Peningkatan rasio magnetoresistance pada paduan ini diharapkan dapat memberikan dampak positif bagi perkembangan paduan ini untuk aplikasi selanjutnya terutama pada sifat sensitivitasnya.

PENENTUAN STRUKTUR MAGNETIK CaMnO3 DENGAN DIFRAKSI NEUTRON

Jurnal Sains Materi Indonesia Edisi Khusus, Oktober 2006
Publisher : Center for Science & Technology of Advanced Material - National Nuclear Energy Agency of

Show Abstract | Original Source | Check in Google Scholar

Abstract

PENENTUAN STRUKTUR MAGNETIK CaMnO3 DENGAN DIFRAKSI NEUTRON. Informasi mengenai struktur magnetik tidak dapat diperoleh melalui difraksi sinar-X (XRD). Oleh karena itu dibutuhkan data yang berasal dari difraksi neutron. Struktur magnetik CaMnO3 dalam penelitian ini dijelaskan melalui difraksi neutron metode serbuk. Preparasi sampel CaMnO3 mula-mula mencampur bahan dasar melalui perhitungan kimia, setelah itu dilanjutkan melalui proses milling dengan variasi waktu dan variasi pemanasan. Dari hasil karakterisasi melalui difraksi sinar-X diperoleh bahwa, fasa baru CaMnO3 terbentuk pada milling selama 12 jam dan pemanasan 1000 ºC selama 9 jam. Sistem kristal berada pada sistem simetri orthorhombik dengan group ruang (Pnma -D162h) dan parameter kisi (di suhu 12 K), a = 5,2801 Å, b = 7,4432 Å, c = 5,2588 Å. CaMnO3 memiliki suhu Neel di 131 K[3], artinya bahan ini berubah sifat menjadi antiferomagnetik jika berada di bawah suhu Neel. Hasil difraksi neutron CaMnO3, sifat magnetik muncul pada atom Mn di suhu 12 K sudut 2θ=24,486 bidang pantulan hkl (011) dengan struktur magnetik pada atom Mn di posisi simetri 4b(0,0,½) adalah nonkolinear antiferromagnetik dan momen magnetiknya m(Mn) = 1,73 μB.