Analisis Pengaruh Proses Brazing Kuningan Terhadap Perubahan Sifat Mekanis dari Pipa Baja Karbon Rendah Mardiana, Mardiana; Karmiadji, Djoko W.
Majalah Forum Teknik UGM Vol 3, No 3 (2010)
Publisher : Majalah Forum Teknik UGM

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (71.575 KB)

Abstract

Low carbon steel has suitable physical properties such as: easily to be casted, welded andmachined. Generally, this steel is used for construction, hospital and house hold equipment, andso on. Some equipment structures employ low carbon steel pipe for basic construction, in whicha lot of brazing joins are applied for connecting each pipe to form a house hold or hospitalequipment. This research analyzes the brazing methode, since it is commonly used to obtainsmoother joint surface compared with the other method and having lower melting temperaturethan the pipe. The analysis emphasizes the transformation of mechanical characteristics suchas: tensile strength, hardness, micro and macro structures. The result of this research showsthat the maximum tensile strength is 509 N/mm2 when the welded groove is 0,5 mm, or 2,35%greater than welded metal strength, and 12,5% less than base metal strength. The hardnessvalues are decreasing compared with the base metal, i.e., 18,5% of average, 18,57% at HAZ(Heat Afffected Zone), and 19,81% of pipe metal under the value of base metal.Kata kunci: Brazing, pipa baja karbon rendah, sifat mekanis
Desain Gating System dan Parameter Proses Pengecoran untuk Mengatasi Cacat Rongga Poros Engkol Syah, Kadarisman; Karmiadji, Djoko W.; Rahmalina, Dwi
JTERA (Jurnal Teknologi Rekayasa) Vol 2, No 1: June 2017
Publisher : Politeknik Sukabumi

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (875.511 KB) | DOI: 10.31544/jtera.v2.i1.2017.55-62

Abstract

Teknologi pengecoran logam merupakan salah satu metode yang sering digunakan dalam sektor industri pengolahan logam. Pada proses pengecoran poros engkol menggunakan besi cor nodular (FCD 700) juga terkadang timbul cacat pengecoran, salah satunya adalah cacat penyusutan (macro shrinkage). Cacat penyusutan terjadi karena rongga atau lubang yang terbentuk akibat pengecilan volume ketika logam mengalami pembekuan. Pada saat proses pembekuan logam, tiap bagian coran yang berbeda bentuknya atau dimensinya memiliki kecepatan pembekuan yang berlainan. Pada umumnya, cacat penyusutan terjadi pada bagian yang paling tebal dengan laju pembekuan yang paling lambat dan daerah cacat biasanya dikelilingi oleh krital-kristal dendrite yang terjadi pada saat pembekuan logam. Salah satu solusi untuk mendapatkan produk poros engkol yang  bebas dari cacat penyusutan adalah dengan melakukan optimasi desain gating system. Hasil penelitian menunjukkan bahwa desain yang dibuat masih menghasilkan cacat berupa rongga penyusutan. Hal ini terjadi karena belum optimalnya desain sistem saluran yang telah digunakan.
ANALISIS PEMBUATAN PIPA BAJA SISTEM DUA BAGIAN LAS ASTM A139 DENGAN MENGGUNAKAN METODA LSAW = MANUFACTUR ANALYSIS DUAL SEAM WELD STEEL PIPE ASTM A139 BY USING LSAW METHODE Karmiadji, Djoko W.; Setiadi, Gery
Majalah Ilmiah Material, Komponen dan Konstruksi Vol 14, No 1 (2014)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (905.81 KB)

Abstract

One of the main components of the manufacture of steel pipe is in the form of plate steel sheet, slab or hot roll coil, which of these materials may be made for various types of pipes, among others, seamless, Electric Wire Resistance, Spiral and Longitudinal pipes.The main material used welding steel pipe is a steel plate or hot roll coil. Material procurement dependence becomes an obstacle for welding steel pipe mill, which at this moment in our countrys steel mills have not been able to produce material of diameter of 24 "steel pipe used primarily in the oil and gas sector.In this research, the analysis of welded steel pipe manufacture using local plate material consisting of two sections then welded with GMAW and SMAW welding type, where the manufacture of welded steel pipe with dimensions Ø 28 "x 8.7 mm x 12.000 mm is done using the LSAW (Longitudinal Sub Merged Arc Welding) method. Mechanical testing and inspection conducted in accordance with ASTM A139.Based on the analysis of the results of testing and inspection, it can be concluded that the method of manufacture of welded steel pipes using dual seam weld longitudinal submerged arc welding compliant as required in the standard ASTM A139.Keywords : steel pipe, dual seam weld, ASTM A139Abstrak Salah satu komponen utama dari pembuatan pipa baja adalah baja berupa plat lembaran, slab atau hot roll coil, dimana dari bahan ini dapat dibuat berbagai jenis pipa antara lain pipa seamless, pipa Electric Wire Resistance, pipa Spiral, dan Pipa Longitudinal.Material utama pipa baja las yang digunakan adalah plat baja atau hot roll coil. Ketergantungan pengadaan material menjadi kendala bagi pabrik pipa baja las, dimana pada saat ini pabrik baja di negara kita belum mampu memproduksi bahan pipa baja berdiameter lebih dari 24” terutama digunakan pada sektor minyak dan gas.Pada penelitian ini dilakukan analisis pembuatan pipa baja las dengan menggunakan bahan plat lokal yang terdiri dari dua bagian kemudian di las dengan jenis las GMAW dan SMAW, dimana pembuatan pipa baja las dengan dimensi Ø 28” x 8,7 mm x 12.000 mm dilakukan menggunakan metoda LSAW (Longitudinal Sub Merged Arc Welding). Teknik pengujian dan pemeriksaan dilakukan dengan mengacu pada standar ASTM A139.Berdasarkan analisis hasil pengujian dan pemeriksaan, dapat di simpulkan bahwa metode pembuatan pipa baja las menggunakan metode dual seam weld longitudinal submerged arc welding memenuhi persyaratan standar sebagaimana yang dipersyaratkan pada standar ASTM A139.Kata kunci: pipa baja, las dua bagian, ASTM A139