DENSIFICATION OF KAPOK WOOD (CEIBA PENTANDRA L. GAERTN) AND ITS RADIATION CURING OF SURFACE COATINGS USING ULTRA-VIOLET

Jurnal Sains Materi Indonesia Vol 14, No 3 (2013): April 2013
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar

Abstract

Densification and surface coating of kapok wood (Ceiba pentandra L. Gaertn ) have been conducted by pressing and followed by radiation curing of surface coatings using Ultra Violet (UV) light. Pressing was performed to get thickness reduction level of 15, 30, 45, 60 and 75 %. Coating was conducted using unsaturated polyester resin after mixing with 2,2-dimethyl-2-hydroxy acetophenone photoinitiator at concentration level of 1, 2 and 3 %b.w and titanium dioxide pigment. Irradiation was carried out at conveyor speed of 1, 2 and 3 m/minute. Pressing of wood up to 75% thickness reduction resulted in increasing of density significantly and decreasing of thickness swelling. At variation of photoinitiator concentration and conveyor speed used, the coating had pendulum hardness of 23-37 seconds, color value (white) with L = 61-79 %, gloss (60o) = 16-56 %, adhesion met the ASTM standard and resistant to chemicals and solvents used except against 10 % sodium hydroxide solution.Keywords: Densification, Ceiba pentandra L. Gaertn wood, Surface coatings, Ultra Violet radiation

DENSIFIKASI KAYU RANDU (CEIBA PENTANDRA L. GAERTN) DAN PELAPISAN PERMUKAANNYA DENGAN PEMADATAN MENGGUNAKAN RADIASI ULTRA VIOLET

Jurnal Sains Materi Indonesia Vol 14, No 3: APRIL 2013
Publisher : BATAN

Show Abstract | Original Source | Check in Google Scholar | Full PDF (158.539 KB)

Abstract

DENSIFIKASI KAYU RANDU (CEIBA PENTANDRA L. GAERTN) DAN PELAPISAN PERMUKAANNYA DENGAN PEMADATAN MENGGUNAKAN RADIASI ULTRA VIOLET. Proses densifikasi dan pelapisan permukaan kayu randu (Ceiba pentandra L. Gaertn) telah dilakukan dengan metode penekanan dilanjutkan proses pelapisan permukaan dengan pemadatan menggunakan radiasi sinar Ultra Violet (UV). Penekanan dilakukan secara bertahap pada suhu 100 oC untuk mendapatkan variasi pengurangan tebal 15%, 30 %, 45%, 60 %dan 75%dan parameter yang diukur meliputi densitas dan pengembangan tebal kayu. Proses pelapisan dilakukan menggunakan resin poliester tak jenuh setelah dicampur fotoinisiator 2,2-dimetil- 2-hidroksi asetofenon dengan konsentrasi 1 %berat, 2 %berat dan 3 %berat dan bahan pewarna titanium dioksida. Iradiasi dilakukan pada kecepatan konveyor 1 m/menit, 2 m/menit dan 3 m/menit. Penekanan sampai dengan pengurangan tebal 75% meningkatkan densitas secara signifikan danmenurunkan pengembangan tebal. Pada variasi konsentrasi fotoinisiator dan kecepatan konveyor yang dipakai, lapisan mempunyai kekerasan pendulum23 detik hingga 37 detik, nilaiwarna (putih) dengan L = 61%hingga 79%, kilap (60o) = 16%hingga 56%, adesi memenuhi standar ASTMdan tahan bahan kimia dan pelarut yang diujikan kecuali terhadap larutan NaOH 1 %.